Confirm with: GB/T 5293 F4A2-H08A AWS A5.17 F60-EL8 BS EN 756-S 35 2 CS S1 ISO 14171-A-S35 2 CS S1 ISO 14171-B-S43A2 CS SU11
JL-H08A is a submerged arc welding wire of coppersurfaced carbon structural steel, Be used together with fused flux SJ301, SJ301 is silico-calcium neutral agglomerated flux, alkalinity is approx 1.0, It appears a ball granule of gray color about 10~60 mesh in size. They are used together, the arc is stable, slag is easy to remove and bead appearance is excellent. The weld metal is possessed of good mechanical properties.
Model No.: JL-H08A Flux contanining: Containing flux Diameter: ø 2.0mm~ ø 5.0 mm Type: Rolling wire Weight: 25kg, 50kg etc. Typical mechanical properties of deposited metal:
NOTICE: 1. Dry the flux at 300~350° C for 1~2 hours before, completely remove rust, oil and dirt from the groove surface prior to welding. 2. Before welding, rust, water and impurities are to be removed from the welded surfaces of workplaces
Commodity Trade Name Size Batch No. Mfg. Date Applied rules or standards issuance Date of lssue Cerificate No. Submerged Arc JL-H08A 2.5mm 1305675 2014.03 GB/T5293-1999 H08A AWS EL8
-- Requirement 410-550 ≥330 ≥22 ≥27(-20) AW DCEP 250-380 30-40 HJ431 Test Result 490 385 28 55 60 60 AW DCEP 280 34 HJ431
-- Core Wire Heat No
ISO 9001-2008 Registered Quality Managgment System
Remarks : We Hereby Certify ThatThis Report Is Correct A nd That All Test Results Are In Compliance With The Specification Described Herein. .
Confirm with: GB/T 5293 F4A2-H08A AWS A5.17 F60-EL8 BS EN 756-S 35 2 CS S1 ISO 14171-A-S35 2 CS S1 ISO 14171-B-S43A2 CS SU11
JL-H08A is a submerged arc welding wire of coppersurfaced carbon structural steel, Be used together with fused flux SJ301, SJ301 is silico-calcium neutral agglomerated flux, alkalinity is approx 1.0, It appears a ball granule of gray color about 10~60 mesh in size. They are used together, the arc is stable, slag is easy to remove and bead appearance is excellent. The weld metal is possessed of good mechanical properties.
Model No.: JL-H08A Flux contanining: Containing flux Diameter: ø 2.0mm~ ø 5.0 mm Type: Rolling wire Weight: 25kg, 50kg etc. Typical mechanical properties of deposited metal:
NOTICE: 1. Dry the flux at 300~350° C for 1~2 hours before, completely remove rust, oil and dirt from the groove surface prior to welding. 2. Before welding, rust, water and impurities are to be removed from the welded surfaces of workplaces
Commodity Trade Name Size Batch No. Mfg. Date Applied rules or standards issuance Date of lssue Cerificate No. Submerged Arc JL-H08A 2.5mm 1305675 2014.03 GB/T5293-1999 H08A AWS EL8